Preventing erosion in steam distribution piping is generally a more simple matter, and typically requires the removal of water droplets entrained within the steam. This involves the installation of a steam-condensate separator.

Steampipelines

Care instructions adapted under license by your healthcare professional. If you have questions about a medical condition or this instruction, always ask your healthcare professional. Healthwise, Incorporated disclaims any warranty or liability for your use of this information.

Although steam supplied through the boiler can have a high percent of dryness, all boilers without super heater sections still contain certain amounts of condensate entrained in the steam that is created. Condensate also forms from radiation heat loss throughout the distribution piping. For these reasons, it is critically important to both install traps at regular intervals and install separators that mechanically remove water droplets from steam in required areas.

Care instructions adapted under license by your healthcare professional. If you have questions about a medical condition or this instruction, always ask your healthcare professional. Healthwise, Incorporated disclaims any warranty or liability for your use of this information.

Condensate recovery piping in particular can be susceptible to erosion from improperly handled flash steam that occurs in the discharge stream. Indeed, even though condensate piping is designed for condensate transport, the process of flash re-vaporization can result in an environment very similar to steam distribution piping containing a large volume of high velocity wet steam. This type of LDI erosion is often called "flashing erosion".

The gun shoots barbed darts. The darts are connected to the gun by long wires. The electricity sent along the wires to the darts causes muscle spasms. This may have made you fall to the ground.

Steampiping design Handbook PDF

In such cases, the options are to locate the trap further upstream and away from the direction change, eliminate direction changes where possible, over-size the discharge pipe if cost effective, or select a trap with a more continuous type discharge such as a Free Float® or float design.

Follow-up care is a key part of your treatment and safety. Be sure to make and go to all appointments, and call your doctor or nurse advice line (811 in most provinces and territories) if you are having problems. It's also a good idea to know your test results and keep a list of the medicines you take.

Steamboiler piping

Resistance to erosion varies according to the material. For reasons related to cost and installation, carbon steel piping is typically used as standard practice in most steam distribution lines even though it isn't as resistant as stainless steel piping. Use of stainless steel piping is usually limited to pharmaceutical, biotech, clean steam, or other sterile applications.

Calculate and display steam property values using pressure-based saturated steam tables, temperature-based saturated steam tables, and heating steam tables.

Steampipe sizing Calculator

Condensate recovery piping is typically designed using the average rate of condensate flow. However, if steam traps that operate intermittently are used, such as bucket, disc, piston, and thermostatic type traps, then the momentary discharge rate can be much greater than the calculated average. This can result in a much higher condensate flow velocity than anticipated, which may lead to greater erosion of the piping.

Steampipe slope direction

However, once thinning caused by erosion starts to occur, additional thinning of the pipe wall can occur even more rapidly. This is because the high velocity water not only physically breaks down the impacted region of the steel piping, but also accelerates corrosion by removing the surface treatments that protect the piping.

Due to specific volume differences between steam and condensate, the sudden condensation of flash steam can create a large void that is rapidly and often violently filled by adjacent condensate, thereby causing shock waves known as water hammer. The rapid collapse of the flash volume and associated shock caused by high velocity condensate filling the void can lead to significant piping erosion and damage.

Limiting erosion in condensate recovery piping requires multiple design considerations. One crucial element is to size the condensate return pipe large enough to accommodate steam and condensate two-phase flow, as discussed here:

Steampipe Specification pdf

Water both entrained in steam flow and also as non-discharged condensate traveling at high speeds in piping is the source of most erosion. By repeatedly impacting piping at bends, the water can cause the gradual thinning of the pipe wall due to its mass and high velocity of impact, similar to what occurs in industrial water jet cutting. This type of erosion - caused by water droplets - is typically known as Liquid Droplet Impingement (LDI) Erosion.

Clinical Review BoardAll Healthwise education is reviewed by a team that includes physicians, nurses, advanced practitioners, registered dieticians, and other healthcare professionals.

Erosion is a physical process that refers to the gradual wearing away of a solid through abrasion. This article will focus on erosion in steam and condensate piping, a common problem in steam plants wherein sections of piping are eroded away causing significant steam leakage.

Stun guns may cause other medical problems such as burns and muscle problems. Your muscles may be sore for a day or two.

Steampiping material

Additionally, "cavitation erosion" can occur from the sudden shock wave impacts caused by the implosion of small liquid-free zones within condensate. Cavitation erosion occurs because flash steam can occupy a very large volume, but then suddenly and rapidly condense after a portion of its heat is lost, having been transferred to the adjacent fluid or piping.

©2006-2024 Healthwise, Incorporated. Healthwise, Healthwise for every health decision, and the Healthwise logo are trademarks of Healthwise, Incorporated.

Steampiping DIAGRAM

Erosion in steam and condensate piping is not limited to the above-mentioned erosion caused by liquid droplet impingement (LDI) or high velocity dis-entrained condensate.

In many cases, but particularly with carbon steel piping, erosion can remove the protective inner piping surface treatment thereby speeding the electrochemical thinning of the pipe wall, a process know as corrosion. In fact, both erosion and corrosion typically work together to cause the thinning of the steam pipe inner wall.

Some surface treatments can offer carbon steel piping protections against corrosion, but these aren't as resistant as those for stainless steel. The treatments can temporarily protect the steel to slow down erosion and corrosion.